304 304L stainless steel bar

Stainless Steel Bar

304 stainless steel is a common material in stainless steel, with a density of 7.93 g / cm ³; It is also called 18 / 8 stainless steel in the industry, which means that it contains more than 18% chromium and more than 8% nickel; High temperature resistance of 800 ℃, with good processing performance and high toughness, it is widely used in industry, furniture decoration industry and food and medical industry. However, it should be noted that the content index of food grade …

Send Email
Request Samples

Product introduction

细节  (26).jpg

physical property

Tensile strength σ b (MPa)≥515-1035

Conditional yield strength σ 0.2 (MPa)≥205

Elongation δ 5 (%)≥40

Reduction of area ψ  (%)≥?

Hardness: ≤ 201hbw; ≤92HRB; ≤210HV

Density (20 ℃, g / cm ³): seven point nine three

Melting point (℃): 1398 ~ 1454

Specific heat capacity (0 ~ 100 ℃, kJ · kg-1k-1): 0.50

Thermal conductivity (w · M-1 · k-1): (100 ℃) 16.3, (500 ℃) 21.5

Linear expansion coefficient (10-6 · k-1): (0 ~ 100 ℃) 17.2, (0 ~ 500 ℃) 18.4

Resistivity (20 ℃, 10-6 Ω· m2 / M): 0.73

Longitudinal elastic modulus (20 ℃, kn / mm2): 193


Application

Products are widely used in construction, machinery, coal mining, chemical industry, electric power, railway vehicles, automobile industry, highways, bridges, containers, sports facilities, agricultural machinery, petroleum machinery, prospecting machinery, greenhouse construction and other manufacturing industries

FAQ

  • 1. What is the structural composition of stainless steel?

    The corrosion resistance of stainless steel coils decreases as the carbon content increases. Therefore, the carbon content of most stainless steels is low, up to 1.2%, and some steels have a low ωC (carbon content) of even less than 0.03% (such as 00Cr12). The main alloying element in stainless steel coil is Cr (chromium). Only when the Cr content reaches a certain value, the steel has corrosion resistance. Therefore, the goods Cr (chromium) content of at least 10.5%. Stainless steel coil also contains Ni, Ti, Mn, N, Nb, Mo, Si, Cu and other elements.

  • 2. What are the typical uses of stainless steel?

    Most of the requirements for use are to maintain the original appearance of the building for a long time. In determining which type of goods to choose, the main considerations are the required aesthetic standards, the corrosiveness of the local atmosphere and the cleaning system to be used. However, other applications are increasingly seeking structural integrity or impermeability. Examples include roofs and sidewalls of industrial buildings. In these applications, construction cost to the owner may be more important than aesthetics, and the surface may not be very clean. The use of 304 stainless steel coils in dry interior environments is quite effective.

  • 3. Main characteristics of stainless steel

    Weldability. Different product uses have different requirements for weldability. A class of tableware generally does not require weldability, even including some cookware companies. However, most products require raw materials with good weldability, such as second-class tableware, insulation cups, steel pipes, water heaters, water dispensers, etc.

    Corrosion resistance. Most stainless steel coil products require good corrosion resistance, such as Class I or Class II tableware, kitchen utensils, water heaters, water dispensers, etc.

    Polishing performance. In today’s society, stainless steel coil products in the production process are generally polished, only a few products such as water heaters, drinking fountains, etc. do not need to be polished. Therefore, this requires raw materials with good polishing performance.

  • 4. What are the steps and methods of surface treatment and polishing of stainless steel coils?

    1. The need for pre-treatment
    Pretreatment is an important treatment step before the surface of stainless steel coil parts enter surface treatment (including pickling, chemical polishing and electrochemical polishing, electroplating, passivation, black coating, coloring, chemical treatment, etc.). During the forming process of goods parts, the surface may adhere to oil stains, burrs, rough surfaces and oxides. Therefore, before surface treatment, oil stains, burrs, uneven surfaces and oxides must be removed in order to obtain subsequent satisfactory results through processing.

    2. Treatment of removed dirt
    Stainless steel coil surface pretreatment in the need to remove the dirt can be divided into two categories: organic and inorganic substances.
    (1) organic dirt. Including mineral oil (such as diesel, oil, paraffin, gypsum, etc.) and animal oil, vegetable oil (such as soybean oil, camellia oil, rapeseed oil, lard, butter, etc.). These oils are mainly from the stainless steel coil zero cattle processing process used in the lubricant. , cutting oil, quenching oil, polishing paste and polishing paste, and fingerprints.
    (2) Inorganic dirt. Including dirt, dust particles, oxides and other contaminants generated during the heat treatment process.

    3. Pretreatment steps for stainless steel coil parts
    (1) The surface is mechanically leveled. Eliminate the roughness of the stainless steel coil surface, through mechanical polishing and grinding to achieve a surface finish.
    (2) Degreasing. Remove the surface oil and dirt.
    (3) Acid washing. Remove the oxides on the surface.
    (4) Weak corrosion. Activates the surface to be treated, removes the surface passivation film, and exposes the metal crystal structure.

  • 5. The production process of cold rolled stainless steel coil

    Stainless steel is a high-alloy steel, with a large resistance to rolling deformation. In order to carry out high-efficiency and high-precision rolling, rigid rolling mills should be used, generally multi-roller cold rolling mill.

    Special welding process is also a feature of cold-rolled stainless steel coil production.

    In the production process of cold rolled stainless steel coil, the raw material (hot rolled coil) should be annealed, intermediate annealing should be carried out in the cold rolling process, and the final product should be annealed, so annealing is an important part of the production.

    Cold-rolled stainless steel is a high-grade steel products, there are strict requirements for surface quality. Not only are metallurgical defects caused by the previous process not allowed, but also obvious defects caused by the cold rolling process.

  • Keywords:

Share to:

ONLINE MESSAGE

Send your inquiry / assessment to Us. Anything need us ,please don’t hesitate contact us here! we will keep it secret for you !

ONLINE MESSAGE

Send your inquiry / assessment to Us. Anything need us ,please don’t hesitate contact us here! we will keep it secret for you !